Chromium Doped Yttrium Aluminum Garnet (Cr4+:YAG) Crystal is excellent E-O material for passively Q-switching diode pumped or lamp-pumped Nd:YAG, Nd:YLF, Nd:YVO4 and other Nd (or Yb) doped lasers at wavelength 0.8~1.2µm. With diverse advantages of chemically
stable, durable, UV resistant, good thermal conductivity, high damage threshold ( >500 MW/cm2) and easy to be operated,
Cr4+:YAG is edging out traditional materials, such as LiF, organic Dye and color centers.
THATSHIGH Specifications for Cr4+: YAG Crystal
Dimensions | Surface Area | 2×2 mm2 ~ 14×14mm2 |
Length | 0.1mm ~ 12mm | |
Doping Concentration | 0.05mol% ~ 0.6mol% | |
Initial Transmission | 5% ~ 95% | |
Flatness | < λ/10 @633nm | |
Wavefront Distortion | < λ/6 @633nm | |
Parallelism | < 30" | |
Surface Quality [S/D] | 10/5 | |
AR-coating | R<0.2% @ 1064 nm |
THATSHIGH Cr4+:YAG Crystal Main Features
Simple to use; No need of any external driving system.
Compact setup.
Working frequency as high as 10kHz.
Chromium Doped Yttrium Aluminum Garnet (Cr4+:YAG) Crystal is excellent E-O material for passively Q-switching diode pumped or lamp-pumped Nd:YAG, Nd:YLF, Nd:YVO4 and other Nd (or Yb) doped lasers at wavelength 0.8~1.2µm. With diverse advantages of chemically
stable, durable, UV resistant, good thermal conductivity, high damage threshold ( >500 MW/cm2) and easy to be operated,
Cr4+:YAG is edging out traditional materials, such as LiF, organic Dye and color centers.
THATSHIGH Specifications for Cr4+: YAG Crystal
Dimensions | Surface Area | 2×2 mm2 ~ 14×14mm2 |
Length | 0.1mm ~ 12mm | |
Doping Concentration | 0.05mol% ~ 0.6mol% | |
Initial Transmission | 5% ~ 95% | |
Flatness | < λ/10 @633nm | |
Wavefront Distortion | < λ/6 @633nm | |
Parallelism | < 30" | |
Surface Quality [S/D] | 10/5 | |
AR-coating | R<0.2% @ 1064 nm |
THATSHIGH Cr4+:YAG Crystal Main Features
Simple to use; No need of any external driving system.
Compact setup.
Working frequency as high as 10kHz.